 TPE Versaflex™ G2705 N, 热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生

 
医疗级TPE, 医疗/护理用品, ISO 10993，USP 第 VI 类
 
Versaflex™ G2705 N
热塑性弹性体
 
普立万公司
 
Technical Data
 
产品说明
Versaflex™ G2705 N is an easy processing material designed for applications where FDA regulations are required. The material exhibits high resilience, low compression set, and good puncture resealing characteristics. It is also steam sterilizable.
 
Versaflex™ G2705 N supplied as a dense pellet.
 
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet
搜索 UL 黄卡 •  普立万公司
• Versaflex™
供货地区 • 北美洲 • 拉丁美洲 • 亚太地区
• 非洲和中东 • 欧洲
机构评级 • FDA 未评级 • ISO 10993 Part 5
• ISO 10993 Part 4 • USP 第 VI 类 2
RoHS 合规性 • RoHS 合规
外观 • 半透明
形式 • 粒子
加工方法 • 挤出 • 注射成型
 
物理性能 额定值(英制) 额定值(公制) 测试方法
密度 / 比重 0.890 0.888g/cm³ ASTM D792
弹性体 额定值(英制) 额定值(公制) 测试方法
拉伸应力 4, 5 (300%应变) 528psi 3.64MPa ASTM D412
抗张强度 4, 5 (断裂) 670psi 4.62MPa ASTM D412
伸长率 4, 5 (断裂) 470% 470% ASTM D412
撕裂强度 4, 5 129lbf/in 22.6kN/m ASTM D624
压缩永久变形
73°F (23°C) 20% 20% ASTM D395
158°F (70°C), 22 hr 43% 43% ASTM D395B
硬度 额定值(英制) 额定值(公制) 测试方法
肖氏硬度 5 (邵氏 A, 10 秒, 73°F (23°C)) 60 60 ASTM D2240
充模分析 额定值(英制) 额定值(公制) 测试方法
表观粘度 (392°F (200°C), 11200 sec^-1) 14.9Pa·s 14.9Pa·s ASTM D3835
注射 额定值(英制) 额定值(公制)
料筒后部温度 340 到 390°F 171 到 199°C
料筒中部温度 360 到 420°F 182 到 216°C
料筒前部温度 360 到 420°F 182 到 216°C
射嘴温度 380 到 440°F 193 到 227°C
模具温度 80 到 120°F 27 到 49°C
背压 100 到 200psi 0.689 到 1.38MPa
螺杆转速 25 到 100rpm 25 到 100rpm
 
 
Versaflex™ G2705 N
热塑性弹性体
普立万公司
 
注射说明
Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).
 
Regrind levels up to 20% can be used with Versaflex™ G2705 N with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.
 
Versaflex™ G2705 N has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.
 
Drying is not Required
Injection Speed: 1 to 3 in/sec
1st Stage - Boost Pressure: 350 to 900 psi
2nd Stage - Hold Pressure: 30% of Boost
Hold Time (Thick Part): 3 to 10 sec
Hold Time (Thin Part): 1 to 3 sec
挤出 额定值(英制) 额定值(公制)
熔体温度 375 到 460°F 191 到 238°C
口模温度 375 到 460°F 191 到 238°C
挤压说明
 
Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE or polypropylene (PP)
 
Drying is not required.
Screw Speed = 100-700 RPM
 
 
 
 
 
TPE Versaflex™ G2705 N, 热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生